Sikadur 22, Lo Mod FS (Fast Set) - Low modulus fast setting overlay epoxy

Mfr.: Sika
Item #: I097415
Mfr. #: 444479
*
Pickup at Corona | Change Delivering to 92111 | Change

Price: $657.80
i h h

Description

Low-modulus, fast setting, medium-viscosity, 2-component epoxy resin binder for skid-resistant broadcast overlays and epoxy mortar patching. Conforms to ASTM C-881 Type III, Grade 1, Class C and AASHTO M-235.
  • Fast setting for quick turnaround
  • Meets 3 h/1000 psi requirement when mixed as epoxy mortar
  • Moisture tolerant before and after cure
  • Easy mix ratio A:B = 1:1 by volume
  • Leveling viscosity for efficient broadcast overlay application

Features

  • 100% solids, moisture-tolerant epoxy resin binder
  • Fast setting for quick turnaround
  • Tolerant to moisture both before and after cure
  • Convenient easy mix ratio A:B = 1:1 by volume
  • Excellent strength development

Specifications


Chemical BaseEpoxy ResinShelf Life24 months in original, unopened containers
Storage ConditionsStore dry at 40-95 degF (4-35 degC); condition at 65-8VOC Content<20 g/L
ViscosityApproximately 2,000 cpsShore D Hardness72 (ASTM D-2240) at 73 degF (23 degC), 50% R.H.
Compressive Strength 3h 40F1750 psiCompressive Strength 3h 73F3600 psi
Compressive Strength 3h 90F6400 psiCompressive Strength 8h 40F2000 psi
Compressive Strength 8h 73F4400 psiCompressive Strength 8h 90F6400 psi
Compressive Strength 1d 40F4500 psiCompressive Strength 1d 73F6500 psi
Compressive Strength 1d 90F8000 psiCompressive Strength 3d 40F5500 psi
Compressive Strength 3d 73F7500 psiCompressive Strength 3d 90F8500 psi
Compressive Strength 7d 40F8500 psiCompressive Strength 7d 73F8500 psi
Compressive Strength 7d 90F9000 psiCompressive Strength 14d 40F9000 psi
Compressive Strength 14d 73F9000 psiCompressive Strength 14d 90F9000 psi
Compressive Strength 28d 40F9000 psiCompressive Strength 28d 73F9000 psi
Compressive Strength 28d 90F9000 psiModulus of Elasticity in Compression 7d40,000 psi
Modulus of Elasticity in Compression 28d40,000 psiTensile Strength Neat 7d2650 psi
Tensile Strength Mortar 13 7d1200 psiTensile Adhesion Strength Neat 1d> 550 psi (concrete failure)
Tensile Adhesion Strength Neat 7d> 570 psi (concrete failure)Shear Strength Neat 7d3430 psi
Shear Strength Mortar 13 7d2600 psiThermal CompatibilityPass (ASTM C-884)
Abrasion Resistance Neat 14d0.030 grams weight lossAbrasion Resistance Mortar 13 14d2.0 grams weight loss
Water Absorption Neat 7d< 0.20%Rapid Chloride Permeability0 coulombs (AASHTO T-277)
Mixing RatioComponent A : Component B = 1:1 by volumePot LifeApproximately 15-20 minutes (60 gram mass; ASTM C-
Coverage1 gal. yields 231 in3; mortar binder with 5 gal. sColorClear to light amber
*
*
*