  • Sikadur 32, Hi-Mod LPL - High Modulus, high strength epoxy bonding agent with a Long Pot Life

Sikadur 32, Hi-Mod LPL - High Modulus, high strength epoxy bonding agent with a Long Pot Life

Mfr.: Sika
Item #: I097419
Mfr. #: 403004
*
Pickup at Corona | Change Delivering to 92111 | Change

Price: $201.85
i h h

Description

High-modulus, high-strength, extended pot life, epoxy bonding/grouting adhesive. It is a multi-purpose, 2-component, 100% solids, moisture-tolerant, structural epoxy adhesive.
  • Extended pot life and contact time at elevated temperatures
  • High-strength bonding/grouting adhesive
  • Tolerant of moisture before, during, and after cure
  • Excellent adhesion to most structural materials
  • Convenient easy-to-mix ratio A:B = 1:1 by volume

Features

  • Extended pot life and contact time at elevated temperatures
  • High-strength bonding/grouting adhesive
  • Tolerant of moisture before, during, and after cure
  • Excellent adhesion to most structural materials
  • Easy-to-use for bonding/grouting applications

Specifications


Shelf Life24 monthsStorage ConditionsStore dry at 40-95 degF (4-35 degC)
ViscosityApproximately 2,800 cpsCompressive Strength (1 day at 40F)-
Compressive Strength (3 day at 73F)10,700 psi (73.8 MPa)Compressive Strength (7 day at 40F)2,500 psi (17.2 MPa)
Compressive Strength (7 day at 73F)11,000 psi (75.9 MPa)Compressive Strength (14 day at 40F)8,300 psi (57.2 MPa)
Compressive Strength (14 day at 73F)12,000 psi (82.3 MPa)Compressive Strength (28 day at 40F)10,000 psi (68.9 MPa)
Compressive Strength (28 day at 73F)13,000 psi (89.7 MPa)Modulus of Elasticity in Compression2.6 x 10^5 psi (1,794 MPa)
Flexural Strength9,100 psi (62.8 MPa)Modulus of Elasticity in Flexure7.3 X 10^5 psi (5,037 MPa)
Tensile Strength5,800 psi (40.0 MPa)Shear Strength6,400 psi (44.1 MPa)
Slant Shear Strength (plastic concrete to hardene2,200 psi (15.2 MPa)Slant Shear Strength (plastic concrete to steel)2,200 psi (15.2 MPa)
Slant Shear Strength (hardened concrete to harden2,900 psi (20 MPa)Heat Deflection Temperature108 degF (42 degC)
Water Absorption0.15 %Mixing RatioComponent A : Component B = 1:1 by volume
Pot Life at 73FApproximately 90 minutesPot Life at 100FApproximately 60 minutes
Contact Time (substrate 40F material 73F)10-14 hContact Time (substrate 73F material 73F)6-7 h
Contact Time (substrate 90F material 73F)2-2.5 hContact Time (substrate 40F material 100F)6-8 h
Contact Time (substrate 73F material 100F)5-6 hContact Time (substrate 90F material 100F)1.5-2 h
ColorDark grayPackaging1 (3.8 L) and 4 gal. (15.1 L) units
*
*
*