EG-96 HP is a three component, 100% solids, VOC and BGE free epoxy resin system designed for pours from 1 inch to 8 inch. It offers rapid strength development, excellent flow characteristics, and good resistance to impact and vibratory loading.
  • High early strength
  • Excellent creep resistance
  • Thermal stability during application
  • Excellent adhesion to concrete and steel
  • High degree of chemical resistance

Features

  • Three component, 100% solids epoxy resin system
  • Designed for deep grouting of large machine bases and precision alignment
  • Suitable for aggressive chemical environments
  • Economical for large volume applications
  • Adjustable flow to meet various onsite conditions

Includes

  • Part A Epoxy Resin: 27.1 lb. (12.3 kg) in 5 gal. plastic pail
  • Part B Hardener: 5.9 lb. (2.7 kg) in 1 gal. metal can
  • Part C Aggregate: Five 48 lb. (21.8 kg) bags (240 lb. total)

Specifications


ColorGray to Light GrayWorking Time45 Minutes
Initial SetGel Time @ 50F8 - 10 HoursInitial SetGel Time @ 72F90 Minutes
Initial SetGel Time @ 90F60 MinutesPeak Exotherm (5 bags per Mix)82 degF (28 degC)
Peak Exotherm (4 bags per Mix)88 degF (31 degC)Maximum Depth of Pour8 inch (20 cm)
Maximum Service Temperature180 degF (82 degC)Specific Weight (5 bags)2.19 g/cm3
Specific Weight (4 bags)2.14 g/cm3Compressive Strength @ 8 hours (5 bags)3,600 psi (25 MPa)
Compressive Strength @ 8 hours (4 bags)3,800 psi (26 MPa)Compressive Strength @ 16 hours (5 bags)9,000 psi (62 MPa)
Compressive Strength @ 16 hours (4 bags)9,150 psi (63 MPa)Compressive Strength @ 1 Day (5 bags)11,400 psi (79 MPa)
Compressive Strength @ 1 Day (4 bags)11,200 psi (77 MPa)Compressive Strength @ 3 Days (5 bags)13,300 psi (92 MPa)
Compressive Strength @ 3 Days (4 bags)13,000 psi (90 MPa)Compressive Strength @ 7 Days (5 bags)14,400 psi (99 MPa)
Compressive Strength @ 7 Days (4 bags)15,000 psi (114 MPa)Compressive Strength @ 28 Days (5 bags)15,200 psi (105 MPa)
Compressive Strength @ 28 Days (4 bags)16,000 psi (110 MPa)Compressive Modulus (5 bags)590,800 psi (4074 MPa)
Compressive Modulus (4 bags)589,600 psi (4066 MPa)Tensile Strength2,900 psi (20 MPa)
Tensile Elongation @ Break0.66%Flexural Strength6,300 psi (43 MPa)
Bond Strength to Concrete> 550 psi (3.8 MPa) Concrete FailureBond Strength to Steel2,500 psi (17.2 MPa)
Coefficient of Thermal Expansion17.4 x 10^-6 / degCHardness Shore D92
Heat Distortion Temperature136 degF (58 degC)
*
*
*